Barium Borate ( BBO ) Crystal

Products > Crystal Products > Barium Borate ( BBO ) Crystal

Barium Borate ( BBO ) Crystal

High Temperature form BBO (a-BaB2O4) is a negative uniaxial crystal. Following exceptional properties make it a very important nonlinear crystal: 

Product Presentation 

High Temperature form BBO (a-BaB2O4) is a negative uniaxial crystal. Following exceptional properties make it a very important nonlinear crystal:

Advantage:

· Broad phase-matching range from 410 nm to 3500 nm

· Useful optical transmission from 190 nm to 3500 nm

· High optical homogeneity with dn » 10-6/cm

· Wide temperature-bandwidth of about 55°C

· High damage threshold of 10 GW/cm2 for 100ps pulse-width at 1064nm

· Low thermo-optic coefficient

Applictions:

· Second, third, fourth and fifth harmonic generation of Nd doping lasers

· Frequency double, tripling and mixing of dye and Ti :Sapphire lasers

· Optical parametric amplifier (OPA) and optical parametric oscillators (OPO)

· Frequency double, tripling and mixing of Dye and Ti :Sapphire lasers

· Frequency-doubling of Argon ion, Cu-vapor and Ruby lasers

· Research and development for advanced laser techniques, including all-solid state wide-tunabl
lasers, ultrafast pulse lasers, and DUV lasers. 

Chemical and Structural properties of BBO:

Crystal Structure:

Trigonal, space group R3c

Lattics Parameters:

a=b=12.532Å, c=12.717Å, Z=6

Melting Point

About 1095℃

Mohs Hardness

4

Density 

3.85g/cm3

Thermal Conductivity

1.2W/m/K(┴c): 1.6W/m/K(//c)

Thermal Expansion Coefficients

 a11=4x10-6/K;  a33=36x10-6/K

Optical and Nontinear Optical Properties Of BBO:

Transparency Range:

190-3500nm

SHG Phase Matchable Range

409.6-3500nm(Type I)    525-3500nm(Type II)

Therm-optic Coefficients(/℃)

dno/dT=-16.6X10-6 , dne/dT=-9.3X10-6

Absorption Coefficients

<0.1%/cm at 1064nm ,        <1%/cm at 532nm

Angle Acceptance

0.8mrad-cm  (θ, Type I,1064 SHG) ,
1.27mrad-cm (θ, Type II,1064 SHG)

Temperature Acceptance

55℃-cm

Spectral Acceptance

1.1nm-cm

Walk-off Angle

2.7°(Type I 1064 SHG), 3.2°(Type II 1064 SHG)

NLO Coefficients

deff (I)=d31sinθ+(d11cosΦ-d22sin3Φ)cosθ
deff (II)=(d11sin3Φ+d22cos3Φ)cos2θ

Non-vanished NLO susceptibilities

d11=5.8xd36(KDP), d31=0.05xd11, d22<0.05xd11

Sellmeier Equations (λ in μm )

no2=2.7359+0.01878 / (λ2-0.01822) -0.01354 λ2
ne2=2.3753+0.01224 / (λ2-0.01667) -0.01516 λ2

Electro-optic coefficients:

r22=2.7pm/V

Resistivity:

>1011 ohm-cm