KDP&K*DP

KDP&K*DP

KDP and KD*P are among the most widely-used commercial NLO materials, characterized by good UV transmission, high damage threshold, and high birefringence.

 They are usually used for doubling, tripling and quadrupling of a Nd:YAG laser at the room temperature. In addition, they are

 also excellent electro-optic crystals with high electro-optic coefficients, widely used as electro-optical modulators, such as Q- switches, Pockels Cells, etc. 

Product Presentation

Applications:

u       Second, third, and fourth harmonic generation of Nd:lasers. 

u       Frequency doubling of dyer laser 

u       High power laser frequency conversion materials 

u       Shutter for high speed photography 

u       Electro-optical modulator and Q switches 


Baisc properties:

  Chemical Formula 

KH2PO4
KDP

KD2PO4
KD*P 

 Transparency range, μm 

0.174-1.57 

0.2-2.1 

 Symmetry class 

42m 

42m 

 Lattice parameters,A

a=b=7.453; c=6.975 

a=b=7.469; c=6.976 

 Density, g/cm3

2.338 

2.355 

 Mohs hardness 

2.5 

2.5 

 Refractive index at 407.8 nm : 

no =1.52301; ne =1.47898 

no =1.5185; ne=1.4772 

  at 632.8 nm 

no =1.50737; ne =1.46685 

no =1.5044; ne=1.4656 (at 623.4 nm) 

  at 1064 nm 

no =1.4938; ne =1.4599 

no =1.4948; ne=1.4554 

Non-linear coefficient at 1.064 μm, pm/V 

d36 = 0.39 

d36 = 0.37 

 Optical damage threshold,  MW/cm2 

300-600 (1064 nm, 20   ns) 

>100 (1064 nm, 20 ns) 